S-Plastic Thermocomp TF006 resin is LNP Thermocomp FF-1006 is a glass fiber filled Polyurethane.

Product Categories

Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

Shenzhen Samtion Chemical Co., Ltd

Contact Now

S-Plastic Thermocomp TF006 resin is LNP Thermocomp FF-1006 is a glass fiber filled Polyurethane.

Name: SPlastic Thermocomp TF006 resin is LNP Thermocomp FF1006 is a glass fiber filled Polyurethane
Brand: S-Plastic Thermocomp
Price: 1 USD

China S-Plastic Thermocomp TF006 resin is LNP Thermocomp FF-1006 is a glass fiber filled Polyurethane. wholesale

Brand Name : S-Plastic Thermocomp

Model Number : TF006

Certification : Datasheet，MSDS，ROHS，SGS，REACH，FDA，EU，UL，COC/COA ,please contact us

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Thermocomp TF006 resin is LNP Thermocomp FF-1006 is a glass fiber filled Polyurethane.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	77	MPa	ASTM D 638
Tensile Stress, break	76	MPa	ASTM D 638
Tensile Stress, yld, Type I, 5 mm/min	50	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	49	MPa	ASTM D 638
Tensile Strain, yield	19.2	%	ASTM D 638
Tensile Strain, break	21.5	%	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	16.3	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	16	%	ASTM D 638
Tensile Modulus, 50 mm/min	1480	MPa	ASTM D 638
Flexural Stress	71	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	58	MPa	ASTM D 790
Flexural Modulus	2060	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	1690	MPa	ASTM D 790
Tensile Stress, yield	69	MPa	ISO 527
Tensile Stress, break	69	MPa	ISO 527
Tensile Stress, yield, 5 mm/min	51	MPa	ISO 527
Tensile Stress, break, 5 mm/min	51	MPa	ISO 527
Tensile Strain, yield	13.7	%	ISO 527
Tensile Strain, break	15.5	%	ISO 527
Tensile Strain, yield, 5 mm/min	15.5	%	ISO 527
Tensile Strain, break, 5 mm/min	16	%	ISO 527
Tensile Modulus, 1 mm/min	1800	MPa	ISO 527
Flexural Stress	66	MPa	ISO 178
Flexural Modulus	2580	MPa	ISO 178
Flexural Modulus, 2 mm/min	2180	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	NB1751	J/m	ASTM D 4812
Izod Impact, notched, 23°C	512	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	19	J	ASTM D 3763
Multiaxial Impact	17	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	131	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	41	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	167	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	78	°C	ASTM D 648
CTE, -40°C to 40°C, flow	2.7E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	1.3E-04	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	2.84E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.31E-04	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	167	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	85	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.47	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.36	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.1 - 0.4	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.5 - 0.8	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.15	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.4	%	ISO 294
Density	1.47	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.5	%	ISO 62
Source GMD, last updated:10/02/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.03	%
Melt Temperature	210 - 215	°C
Front - Zone 3 Temperature	205 - 215	°C
Middle - Zone 2 Temperature	200 - 210	°C
Rear - Zone 1 Temperature	190 - 200	°C
Mold Temperature	15 - 55	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:10/02/2004

Other related products we recommend:

For more information please download the datasheet
	S-Plastics Thermocomp TF006.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

S-Plastic Thermocomp TF006 resin is LNP Thermocomp FF-1006 is a glass fiber filled Polyurethane.