S-Plastic Thermocomp LX08411 is a compound based on Polyetheretherketone resin containing Carbon Fiber.

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

Shenzhen Samtion Chemical Co., Ltd

Contact Now

S-Plastic Thermocomp LX08411 is a compound based on Polyetheretherketone resin containing Carbon Fiber.

Name: SPlastic Thermocomp LX08411 is a compound based on Polyetheretherketone resin containing Carbon Fiber
Brand: S-Plastic Thermocomp
Price: 1 USD

China S-Plastic Thermocomp LX08411 is a compound based on Polyetheretherketone resin containing Carbon Fiber. wholesale

Brand Name : S-Plastic Thermocomp

Model Number : LX08411

Certification : Datasheet，MSDS，ROHS，SGS，REACH，FDA，EU，UL，COC/COA ,please contact us

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Thermocomp LX08411 resin is a compound based on Polyetheretherketone resin containing Carbon Fiber.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	270	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	270	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	1.8	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.8	%	ASTM D 638
Tensile Modulus, 50 mm/min	23510	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	366	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	366	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	25000	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	775	J/m	ASTM D 4812
Izod Impact, notched, 23°C	70	J/m	ASTM D 256
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	341	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	327	°C	ASTM D 648
PHYSICAL	Value	Unit	Standard
Density	1.45	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.03	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)	0.2 - 0.28	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	0.75 - 0.85	%	ASTM D 955
Source GMD, last updated:2010/07/12

Processing

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

Other related products we recommend:

For more information please download the datasheet
	S-Plastics Thermocomp LX08411.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

S-Plastic Thermocomp LX08411 is a compound based on Polyetheretherketone resin containing Carbon Fiber.