S-Plastic Stat-kon ZE004 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber.

Product Categories

Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

Shenzhen Samtion Chemical Co., Ltd

Contact Now

S-Plastic Stat-kon ZE004 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber.

Name: SPlastic Statkon ZE004 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber
Brand: S-Plastic Stat-kon
Price: 1 USD

China S-Plastic Stat-kon ZE004 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber. wholesale

Brand Name : S-Plastic Stat-kon

Model Number : ZE004

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon ZE004 resin is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	80	MPa	ASTM D 638
Tensile Stress, break	104	MPa	ASTM D 638
Tensile Strain, break	0.5	%	ASTM D 638
Tensile Modulus, 50 mm/min	24820	MPa	ASTM D 638
Flexural Stress	179	MPa	ASTM D 790
Flexural Modulus	24130	MPa	ASTM D 790
Tensile Stress, yield	54	MPa	ISO 527
Tensile Stress, break	103	MPa	ISO 527
Tensile Strain, break	0.9	%	ISO 527
Tensile Modulus, 1 mm/min	14720	MPa	ISO 527
Flexural Stress	151	MPa	ISO 178
Flexural Modulus	12700	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	299	J/m	ASTM D 4812
Izod Impact, notched, 23°C	37	J/m	ASTM D 256
Izod Impact, unnotched 80104 +23°C	17	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	4	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	139	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	137	°C	ASTM D 648
CTE, -40°C to 40°C, flow	4.86E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	3.6E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	4.8E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	3.7E-05	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	141	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	135	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.17	g/cm³	ASTM D 792
Mold Shrinkage, flow, 24 hrs	0.2 - 0.4	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.4 - 0.6	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.3	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.53	%	ISO 294
Density	1.17	g/cm³	ISO 1183
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+02 - 1.E+06	Ohm	ASTM D 257
Source GMD, last updated:09/24/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	4	hrs
Melt Temperature	300 - 305	°C
Front - Zone 3 Temperature	300 - 310	°C
Middle - Zone 2 Temperature	290 - 300	°C
Rear - Zone 1 Temperature	275 - 290	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/24/2008

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon ZE004.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!