S-Plastic Stat-kon LC-1003 EM is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of

Product Categories

Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

Shenzhen Samtion Chemical Co., Ltd

Contact Now

S-Plastic Stat-kon LC-1003 EM is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of

Name: SPlastic Statkon LC1003 EM is a compound based on Polyetheretherketone resin containing Carbon Fiber Added features of
Brand: S-Plastic Stat-kon
Price: 1 USD

China S-Plastic Stat-kon LC-1003 EM is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of wholesale

Brand Name : S-Plastic Stat-kon

Model Number : LC-1003 EM

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon LC-1003 EM resin is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of this
material include: Easy Molding.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	160	MPa	ASTM D 638
Tensile Strain, break	1.8	%	ASTM D 638
Tensile Modulus, 50 mm/min	11510	MPa	ASTM D 638
Flexural Stress	259	MPa	ASTM D 790
Flexural Modulus	9510	MPa	ASTM D 790
Tensile Stress, break	163	MPa	ISO 527
Tensile Strain, break	1.8	%	ISO 527
Tensile Modulus, 1 mm/min	10520	MPa	ISO 527
Flexural Stress	263	MPa	ISO 178
Flexural Modulus	9850	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	400	J/m	ASTM D 4812
Izod Impact, notched, 23°C	37	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	4	J	ASTM D 3763
Multiaxial Impact	1	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	29	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	4	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	270	°C	ASTM D 648
CTE, -40°C to 40°C, flow	5.2E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	5.36E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	5.19E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	5.36E-05	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	298	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.33	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.07	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.2 - 0.3	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.5 - 0.6	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.28 - 0.31	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.51 - 0.58	%	ISO 294
Density	1.33	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.13	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+03 - 1.E+07	Ohm	ASTM D 257
Source GMD, last updated:10/01/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Maximum Moisture Content	0.1	%
Melt Temperature	380 - 390	°C
Front - Zone 3 Temperature	380 - 395	°C
Middle - Zone 2 Temperature	365 - 375	°C
Rear - Zone 1 Temperature	350 - 360	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60 - 100	rpm
Source GMD, last updated:10/01/2004

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon LC-1003 EM.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!