S-Plastic Stat-kon 9X04323 is a compound based on Noryl GTX resin,Added features of this material include: Electrically Cond

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Stat-kon 9X04323 is a compound based on Noryl GTX resin,Added features of this material include: Electrically Cond

Name: SPlastic Statkon 9X04323 is a compound based on Noryl GTX resinAdded features of this material include Electrically Cond
Brand: S-Plastic Stat-kon
Price: 1 USD

China S-Plastic Stat-kon 9X04323 is a compound based on Noryl GTX resin,Added features of this material include: Electrically Cond wholesale

Brand Name : S-Plastic Stat-kon

Model Number : 9X04323

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon 9X04323 resin is a compound based on Noryl GTX resin,Added features of this material include: Electrically Conductive.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	59	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	56	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	3.7	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	3.7	%	ASTM D 638
Tensile Modulus, 50 mm/min	2760	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	99	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2400	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	59	MPa	ISO 527
Tensile Stress, break, 5 mm/min	58	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	3.5	%	ISO 527
Tensile Strain, break, 5 mm/min	3.5	%	ISO 527
Tensile Modulus, 1 mm/min	2780	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	96	MPa	ISO 178
Flexural Modulus, 2 mm/min	2590	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	32	J/m	ASTM D 256
Izod Impact, notched 80104 +23°C	3	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	180	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	168	°C	ASTM D 648
CTE, -40°C to 40°C, flow	2.2E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	2.4E-05	1/°C	ASTM E 831
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	181	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	163	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.11	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.2	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.93 - 1.24	%	ASTM D 955
Density	1.11	g/cm³	ISO 1183
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+02 - 1.E+04	Ohm	ASTM D 257
Source GMD, last updated:08/05/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	4	hrs
Melt Temperature	300 - 305	°C
Front - Zone 3 Temperature	300 - 310	°C
Middle - Zone 2 Temperature	290 - 300	°C
Rear - Zone 1 Temperature	275 - 290	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:08/05/2008

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon 9X04323.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!