S-Plastic Verton MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material i

Product Categories

Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

Shenzhen Samtion Chemical Co., Ltd

Contact Now

S-Plastic Verton MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material i

Name: SPlastic Verton MV00AS is a compound based on Polypropylene resin containing Long Glass Added features of this material i
Brand: S-Plastic Verton
Price: 1 USD

China S-Plastic Verton MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material i wholesale

Brand Name : S-Plastic Verton

Model Number : MV00AS

Certification : Datasheet，MSDS，ROHS，SGS，REACH，FDA，EU，UL，COC/COA ,please contact us

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Verton MV00AS resin is a compound based on Polypropylene resin containing Long Glass. Added features of this material include:

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	131	MPa	ASTM D 638
Tensile Strain, break	1.8	%	ASTM D 638
Tensile Modulus, 50 mm/min	10440	MPa	ASTM D 638
Flexural Stress	187	MPa	ASTM D 790
Flexural Modulus	9340	MPa	ASTM D 790
Tensile Stress, break	141	MPa	ISO 527
Tensile Strain, break	1.7	%	ISO 527
Tensile Modulus, 1 mm/min	13870	MPa	ISO 527
Flexural Stress	214	MPa	ISO 178
Flexural Modulus	11140	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	208	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	13	J	ASTM D 3763
Multiaxial Impact	13	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	66	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	29	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	157	°C	ASTM D 648
CTE, -40°C to 40°C, flow	3.36E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	4.57E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	3.37E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	4.58E-05	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	164	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	160	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.33	g/cm³	ASTM D 792
Wear Factor Washer	73	10^-10 in^5-min/ft-lb-hr	ASTM D 3702 Modified
Dynamic COF	0.34	-	ASTM D 3702 Modified
Static COF	0.52	-	ASTM D 3702 Modified
Density	1.33	g/cm³	ISO 1183
Source GMD, last updated:10/02/2004

Processing

Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Melt Temperature	220 - 250	°C
Front - Zone 3 Temperature	250 - 260	°C
Middle - Zone 2 Temperature	245 - 255	°C
Rear - Zone 1 Temperature	230 - 245	°C
Mold Temperature	40 - 65	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:10/02/2004

Other related products we recommend:

For more information please download the datasheet
	S-Plastics Verton MV00AS.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

S-Plastic Verton MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material i