S-Plastic Thermocomp EB004 is a compound based on Polyetherimide resin containing Glass Bead.

Name: SPlastic Thermocomp EB004 is a compound based on Polyetherimide resin containing Glass Bead
Brand: S-Plastic Thermocomp
Price: 1 USD

China S-Plastic Thermocomp EB004 is a compound based on Polyetherimide resin containing Glass Bead. wholesale

Brand Name : S-Plastic Thermocomp

Model Number : EB004

Certification : Datasheet，MSDS，ROHS，SGS，REACH，FDA，EU，UL，COC/COA ,please contact us

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Thermocomp EB004 resin is a compound based on Polyetherimide resin containing Glass Bead.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, break	95	MPa	ASTM D 638
Tensile Strain, break	8.8	%	ASTM D 638
Tensile Modulus, 50 mm/min	7580	MPa	ASTM D 638
Flexural Stress	158	MPa	ASTM D 790
Flexural Modulus	4820	MPa	ASTM D 790
Tensile Stress, break	97	MPa	ISO 527
Tensile Strain, break	9.6	%	ISO 527
Tensile Modulus, 1 mm/min	4820	MPa	ISO 527
Flexural Stress	130	MPa	ISO 178
Flexural Modulus	4100	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	411	J/m	ASTM D 4812
Izod Impact, notched, 23°C	37	J/m	ASTM D 256
Izod Impact, unnotched 80104 +23°C	24	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	10	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	198	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	183	°C	ASTM D 648
CTE, -40°C to 40°C, flow	4.5E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	4.32E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	4.4E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	4.3E-05	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	204	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	190	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.43	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.1	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.5 - 0.7	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.6 - 0.8	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.58	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.71	%	ISO 294
Density	1.43	g/cm³	ISO 1183
Source GMD, last updated:09/24/2008

Processing

Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Maximum Moisture Content	0.05	%
Melt Temperature	360 - 365	°C
Front - Zone 3 Temperature	365 - 375	°C
Middle - Zone 2 Temperature	355 - 365	°C
Rear - Zone 1 Temperature	345 - 355	°C
Mold Temperature	120 - 150	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60 - 100	rpm
Source GMD, last updated:09/24/2008
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.

Other related products we recommend:

For more information please download the datasheet
	S-Plastics Thermocomp EB004.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

S-Plastic Thermocomp EB004 is a compound based on Polyetherimide resin containing Glass Bead.