S-Plastic Ultem LTX931A Post Industrial Recycle Based 30% Glass Fiber Filled High Flow Polyetherimide Blend

Product Categories

Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

Shenzhen Samtion Chemical Co., Ltd

Contact Now

S-Plastic Ultem LTX931A Post Industrial Recycle Based 30% Glass Fiber Filled High Flow Polyetherimide Blend

Name: SPlastic Ultem LTX931A Post Industrial Recycle Based 30 Glass Fiber Filled High Flow Polyetherimide Blend
Brand: S-Plastic Ultem
Price: 1 USD

China S-Plastic Ultem LTX931A Post Industrial Recycle Based 30% Glass Fiber Filled High Flow Polyetherimide Blend wholesale

Brand Name : S-Plastic Ultem

Model Number : LTX931A

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Contact Now

S-Plastics Ultem LTX931A resin is Post-industrial recycle based, 30% glass fiber filled, high flow Polyetherimide blend. ECO Conforming.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yield, 5 mm/min	115	MPa	ISO 527
Tensile Stress, break, 5 mm/min	115	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2	%	ISO 527
Tensile Strain, break, 5 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	9200	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	190	MPa	ISO 178
Flexural Modulus, 2 mm/min	8300	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched 80104 +23°C	4	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	4	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	4	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80104 sp=62mm	4	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
CTE, 23°C to 150°C, flow	1.8E-05	1/°C	ISO 11359-2
CTE, 23°C to 150°C, xflow	5.8E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	Passes	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	188	°C	ISO 306
Vicat Softening Temp, Rate B/120	195	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	190	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	184	°C	ISO 75/Ae
PHYSICAL	Value	Unit	Standard
Density	1.52	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.4	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.25	%	ISO 62
Melt Volume Rate, MVR at 360°C/5.0 kg	19	cm³/10 min	ISO 1133
Source GMD, last updated:04/28/2004

Processing

Injection Molding	Value	Unit
Drying Temperature	135	°C
Drying Time	4 - 6	hrs
Drying Time (Cumulative)	24	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	340 - 360	°C
Nozzle Temperature	330 - 355	°C
Front - Zone 3 Temperature	340 - 360	°C
Middle - Zone 2 Temperature	325 - 350	°C
Rear - Zone 1 Temperature	315 - 340	°C
Mold Temperature	135 - 165	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm
Source GMD, last updated:04/28/2004

For more information please download the datasheet
	S-Plastics Ultem LTX931A.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials