| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 168 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 158 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 9300 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 225 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8950 | MPa | ASTM D 790 |
| Hardness, Rockwell M | 114 | - | ASTM D 785 |
| Tensile Stress, yield, 5 mm/min | 165 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 165 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 225 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 427 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 90 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3.2 mm | 491 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 10 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 40 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 227 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 208 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 212 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 210 | °C | ASTM D 648 |
| CTE, -40°C to 150°C, xflow | 6.E-05 | 1/°C | ASTM E 831 |
| CTE, -20°C to 150°C, flow | 2.E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C to 150°C, flow | 2.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 213 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 220 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.51 | - | ASTM D 792 |
| Water Absorption, 24 hours | 0.16 | % | ASTM D 570 |
| Water Absorption, equilibrium, 23C | 0.9 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 0.2 - 0.4 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.2 - 0.4 | % | S-Plastics Method |
| Melt Flow Rate, 337°C/6.6 kgf | 5 | g/10 min | ASTM D 1238 |
| Density | 1.51 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.9 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.5 | % | ISO 62 |
| Melt Volume Rate, MVR at 360°C/5.0 kg | 6 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 3.E+16 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in air, 1.6 mm | 24.8 | kV/mm | ASTM D 149 |
| Dielectric Strength, in oil, 1.6 mm | 30.3 | kV/mm | ASTM D 149 |
| Relative Permittivity, 1 kHz | 3.7 | - | ASTM D 150 |
| Dissipation Factor, 1 kHz | 0.0015 | - | ASTM D 150 |
| Dissipation Factor, 2450 MHz | 0.0053 | - | ASTM D 150 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Oxygen Index (LOI) | 50 | % | ASTM D 2863 |