S-Plastic Ultem HU1004 High Temperature Transparent Polyetherimide Blend With Improved Ductility

Name: SPlastic Ultem HU1004 High Temperature Transparent Polyetherimide Blend With Improved Ductility
Brand: S-Plastic Ultem
Price: 1 USD

China S-Plastic Ultem HU1004 High Temperature Transparent Polyetherimide Blend With Improved Ductility wholesale

Brand Name : S-Plastic Ultem

Model Number : HU1004

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Flow Rate, 337°C/6.6 kgf : 10

Oxygen Index (LOI) : 46

Contact Now

S-Plastics Ultem HU1004 resin is High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant.EtO and steam sterilizable.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	95	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	90	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	7	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	85	%	ASTM D 638
Tensile Modulus, 5 mm/min	2900	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	140	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	3000	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	97	MPa	ISO 527
Tensile Stress, break, 50 mm/min	80	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	7	%	ISO 527
Tensile Strain, break, 50 mm/min	80	%	ISO 527
Flexural Stress, yield, 2 mm/min	136	MPa	ISO 178
Flexural Modulus, 2 mm/min	2800	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	70	J/m	ASTM D 256
Izod Impact, Reverse Notched, 3.2 mm	3300	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	93	J	ASTM D 3763
Instrumented Impact Total Energy, 0°C	99	J	ASTM D 3763
Instrumented Impact Total Energy, -20°C	93	J	ASTM D 3763
Instrumented Impact Ductility, 23°C	100	%	ASTM D 3763
Instrumented Impact Ductility, 0°C	100	%	ASTM D 3763
Instrumented Impact Ductility, -20°C	90	%	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	NB	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80104 -30°C	NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	6	kJ/m²	ISO 180/1A
Charpy Impact, notched, 23°C	11	kJ/m²	ISO 179/2C
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 6.4 mm, unannealed	214	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	204	°C	ASTM D 648
CTE, -20°C to 150°C, flow	5.6E-05	1/°C	ASTM E 831
CTE, -20°C to 150°C, xflow	5.5E-05	1/°C	ASTM E 831
Thermal Conductivity	0.19	W/m-°C	ASTM C 177
CTE, 23°C to 150°C, flow	5.E-05	1/°C	ISO 11359-2
CTE, 23°C to 150°C, xflow	5.E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate A/50	219	°C	ISO 306
Vicat Softening Temp, Rate B/50	212	°C	ISO 306
Vicat Softening Temp, Rate B/120	212	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	205	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	190	°C	ISO 75/Ae
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.28	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.5 - 0.7	%	S-Plastics Method
Melt Flow Rate, 337°C/6.6 kgf	10	g/10 min	ASTM D 1238
Density	1.28	g/cm³	ISO 1183
Melt Volume Rate, MVR at 360°C/5.0 kg	14	cm³/10 min	ISO 1133
FLAME CHARACTERISTICS	Value	Unit	Standard
Oxygen Index (LOI)	46	%	ASTM D 2863
NBS Smoke Density, Flaming, Ds 4 min	0.7	-	ASTM E 662
Source GMD, last updated:10/20/2008

Processing

Injection Molding	Value	Unit
Drying Temperature	150	°C
Drying Time	6 - 8	hrs
Drying Time (Cumulative)	24	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	355 - 390	°C
Nozzle Temperature	345 - 390	°C
Front - Zone 3 Temperature	345 - 390	°C
Middle - Zone 2 Temperature	335 - 390	°C
Rear - Zone 1 Temperature	330 - 390	°C
Mold Temperature	130 - 160	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm
Source GMD, last updated:10/20/2008

For more information please download the datasheet
	S-Plastics Ultem HU1004.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

S-Plastic Ultem HU1004 High Temperature Transparent Polyetherimide Blend With Improved Ductility