| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 139 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 139 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 6890 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 227 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 6890 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 140 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 140 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 5 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 210 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 475 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 64 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 64 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 13 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 225 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 209 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 210 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 211 | °C | ASTM D 648 |
| CTE, -40°C to 150°C, flow | 2.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 150°C, xflow | 6.E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C to 150°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 212 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 218 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 205 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.42 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.3 - 0.5 | % | S-Plastics Method |
| Melt Flow Rate, 337°C/6.6 kgf | 13 | g/10 min | ASTM D 1238 |
| Density | 1.42 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 1 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.55 | % | ISO 62 |
| Melt Volume Rate, MVR at 360°C/5.0 kg | 16 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:10/03/2005 | | |