| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 17 | mg/1000cy | S-Plastics Method |
| Tensile Stress, break, 5 mm/min | 140 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6800 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 210 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6500 | MPa | ISO 178 |
| Hardness, H358/30 | 150 | MPa | ISO 2039-1 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1U |
| Charpy Impact, notched, 23°C | 9 | kJ/m² | ISO 179/2C |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.28 | W/m-°C | ISO 8302 |
| CTE, 23°C to 150°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 223 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 212 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 218 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 205 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.3 - 0.5 | % | S-Plastics Method |
| Density | 1.42 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 1 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.55 | % | ISO 62 |
| Melt Volume Rate, MVR at 360°C/5.0 kg | 10 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 0.8 mm | 34 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 26 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 3 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.0008 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.0025 | - | IEC 60250 |
| Dissipation Factor, 2450 MHz | 0.0049 | - | IEC 60250 |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Comparative Tracking Index, M | 100 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Glow Wire Flammability Index 960°C, passes at | 3.2 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 46 | % | ISO 4589 |
| Source GMD, last updated:10/11/2006 | | |