S-Plastic Ultem 4000 Glass Fiber PTFE And Graphite Filled Standard Flow Polyetherimide (Tg 217C) UL94 V0

Name: SPlastic Ultem 4000 Glass Fiber PTFE And Graphite Filled Standard Flow Polyetherimide Tg 217C UL94 V0
Brand: S-Plastic Ultem
Price: 1 USD

Brand Name : S-Plastic Ultem

Model Number : 4000

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Flow Rate, 337°C/6.6 kgf : 3.1

Contact Now

S-Plastics Ultem 4000 resin is Glass fiber, PTFE, and Graphite filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 listing.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	82	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.2	%	ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span	113	MPa	ASTM D 790
Flexural Stress, brk, 2.6 mm/min, 100 mm span	137	MPa	ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span	8820	MPa	ASTM D 790
Hardness, Rockwell M	85	-	ASTM D 785
Taber Abrasion, CS-17, 1 kg	33	mg/1000cy	ASTM D 1044
PV Limit, 0.51 m/s	2.1	MPa-m/s	S-Plastics Method
K-factor xE-10, PV=2000 psi-fpm vs Steel	62	-	S-Plastics Method
K-factor xE-10, PV=2000 psi-fpm vs Self	1900	-	S-Plastics Method
Coefficient of Friction on steel, Static	0.25	-	ASTM D 1894
Coefficient of Friction on steel,Kinetic	0.24	-	ASTM D 1894
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	160	J/m	ASTM D 4812
Izod Impact, notched, 23°C	64	J/m	ASTM D 256
Izod Impact, Reverse Notched, 3.2 mm	170	J/m	ASTM D 256
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	233	°C	ASTM D 1525
HDT, 1.82 MPa, 6.4 mm, unannealed	212	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.62E-05	1/°C	ASTM E 831
CTE, -20°C to 150°C, flow	1.62E-05	1/°C	ASTM E 831
Relative Temp Index, Elec	105	°C	UL 746B
Relative Temp Index, Mech w/impact	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	105	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.67	-	ASTM D 792
Water Absorption, 24 hours	0.11	%	ASTM D 570
Mold Shrinkage, flow, 3.2 mm	0.2 - 0.3	%	S-Plastics Method
Melt Flow Rate, 337°C/6.6 kgf	3.1	g/10 min	ASTM D 1238
ELECTRICAL	Value	Unit	Standard
Comparative Tracking Index (UL) {PLC}	4	PLC Code	UL 746A
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-0 Flame Class Rating (3)	0.83	mm	UL 94
Source GMD, last updated:01/13/2000

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	135	°C
Drying Time	4 - 6	hrs
Drying Time (Cumulative)	10	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	350 - 370	°C
Nozzle Temperature	350 - 370	°C
Front - Zone 3 Temperature	350 - 370	°C
Middle - Zone 2 Temperature	345 - 365	°C
Rear - Zone 1 Temperature	340 - 360	°C
Mold Temperature	135 - 165	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm
Source GMD, last updated:01/13/2000

For more information please download the datasheet
	S-Plastics Ultem 4000.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

S-Plastic Ultem 4000 Glass Fiber PTFE And Graphite Filled Standard Flow Polyetherimide (Tg 217C) UL94 V0

Product Tags: