S-Plastic Thermocomp LF005 is a compound based on Polyetheretherketone resin containing Glass Fiber.

Product Categories

Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

Shenzhen Samtion Chemical Co., Ltd

Contact Now

S-Plastic Thermocomp LF005 is a compound based on Polyetheretherketone resin containing Glass Fiber.

Name: SPlastic Thermocomp LF005 is a compound based on Polyetheretherketone resin containing Glass Fiber
Brand: S-Plastic Thermocomp
Price: 1 USD

China S-Plastic Thermocomp LF005 is a compound based on Polyetheretherketone resin containing Glass Fiber. wholesale

Brand Name : S-Plastic Thermocomp

Model Number : LF005

Certification : Datasheet，MSDS，ROHS，SGS，REACH，FDA，EU，UL，COC/COA ,please contact us

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Thermocomp LF005 resin is a compound based on Polyetheretherketone resin containing Glass Fiber.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	156	MPa	ASTM D 638
Tensile Stress, break	156	MPa	ASTM D 638
Tensile Strain, yield	2.7	%	ASTM D 638
Tensile Strain, break	2.7	%	ASTM D 638
Tensile Modulus, 50 mm/min	11720	MPa	ASTM D 638
Flexural Stress	248	MPa	ASTM D 790
Flexural Modulus	8960	MPa	ASTM D 790
Tensile Stress, yield	158	MPa	ISO 527
Tensile Stress, break	158	MPa	ISO 527
Tensile Strain, yield	2.6	%	ISO 527
Tensile Strain, break	2.7	%	ISO 527
Tensile Modulus, 1 mm/min	11400	MPa	ISO 527
Flexural Stress	243	MPa	ISO 178
Flexural Modulus	8600	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	934	J/m	ASTM D 4812
Izod Impact, notched, 23°C	90	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	14	J	ASTM D 3763
Multiaxial Impact	3	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	60	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	8	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
CTE, -40°C to 40°C, flow	5.4E-06	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	1.8E-06	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	5.17E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.94E-05	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	239	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.48	g/cm³	ASTM D 792
Mold Shrinkage, flow, 24 hrs	0.5 - 0.7	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1 - 1.2	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.64	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.1	%	ISO 294
Density	1.48	g/cm³	ISO 1183
Source GMD, last updated:09/24/2008

Processing

Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Maximum Moisture Content	0.1	%
Melt Temperature	380 - 390	°C
Front - Zone 3 Temperature	380 - 395	°C
Middle - Zone 2 Temperature	365 - 375	°C
Rear - Zone 1 Temperature	350 - 360	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60 - 100	rpm
Source GMD, last updated:09/24/2008
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.

Other related products we recommend:

For more information please download the datasheet
	S-Plastics Thermocomp LF005.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

S-Plastic Thermocomp LF005 is a compound based on Polyetheretherketone resin containing Glass Fiber.