S-Plastic Thermocomp LCF62E is a compound based on Polyetheretherketone resin containing Carbon and Glass Fiber fillers. Ad

Name: SPlastic Thermocomp LCF62E is a compound based on Polyetheretherketone resin containing Carbon and Glass Fiber fillers Ad
Brand: S-Plastic Thermocomp
Price: 1 USD

Brand Name : S-Plastic Thermocomp

Model Number : LCF62E

Certification : Datasheet，MSDS，ROHS，SGS，REACH，FDA，EU，UL，COC/COA ,please contact us

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Thermocomp LCF63E resin is a compound based on Polyetheretherketone resin containing Carbon and Glass Fiber fillers. Added
features of this material includes: Easy Molding.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	203	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	0.8	%	ASTM D 638
Tensile Modulus, 50 mm/min	62980	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	296	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	17340	MPa	ASTM D 790
Tensile Stress, break, 5 mm/min	196	MPa	ISO 527
Tensile Strain, break, 5 mm/min	0.7	%	ISO 527
Tensile Modulus, 1 mm/min	41090	MPa	ISO 527
Flexural Stress	391	MPa	ISO 178
Flexural Modulus, 2 mm/min	36490	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	711	J/m	ASTM D 4812
Izod Impact, notched, 23°C	80	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	17	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	47	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	8	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	290	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	290	°C	ASTM D 648
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	290	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	290	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.57	-	ASTM D 792
Density	1.57	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.02	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.09 - 2	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1 - 3	%	ASTM D 955
Moisture Absorption (23°C / 50% RH)	0.02	%	ISO 62
Source GMD, last updated:06/19/2008

Processing

Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Maximum Moisture Content	0.1	%
Melt Temperature	380 - 390	°C
Front - Zone 3 Temperature	380 - 395	°C
Middle - Zone 2 Temperature	365 - 375	°C
Rear - Zone 1 Temperature	350 - 360	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60 - 100	rpm
Source GMD, last updated:06/19/2008
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.

Other related products we recommend:

For more information please download the datasheet
	S-Plastics Thermocomp LCF63E.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

S-Plastic Thermocomp LCF62E is a compound based on Polyetheretherketone resin containing Carbon and Glass Fiber fillers. Ad