S-Plastic Stat-kon OEL13I a Linear-PPS base resin containing Carbon Fiber and PTFE Lubricant. Characteristics of this grade

Product Categories

Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

Shenzhen Samtion Chemical Co., Ltd

Contact Now

S-Plastic Stat-kon OEL13I a Linear-PPS base resin containing Carbon Fiber and PTFE Lubricant. Characteristics of this grade

Name: SPlastic Statkon OEL13I a LinearPPS base resin containing Carbon Fiber and PTFE Lubricant Characteristics of this grade
Brand: S-Plastic Stat-kon
Price: 1 USD

China S-Plastic Stat-kon OEL13I a Linear-PPS base resin containing Carbon Fiber and PTFE Lubricant. Characteristics of this grade wholesale

Brand Name : S-Plastic Stat-kon

Model Number : OEL13I

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon OEL13I resin is a Linear-PPS base resin containing Carbon Fiber and PTFE Lubricant. Characteristics of this grade are High Impact.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	132	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.8	%	ASTM D 638
Tensile Modulus, 50 mm/min	13950	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	195	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	10510	MPa	ASTM D 790
Tensile Stress, break, 5 mm/min	130	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.4	%	ISO 527
Tensile Modulus, 1 mm/min	16590	MPa	ISO 527
Flexural Stress	218	MPa	ISO 178
Flexural Modulus, 2 mm/min	11920	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	601	J/m	ASTM D 4812
Izod Impact, notched, 23°C	93	J/m	ASTM D 256
Multiaxial Impact	3	J	ISO 6603
Instrumented Impact Total Energy, 23°C	16	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	35	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	8	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	273	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	213	°C	ASTM D 648
CTE, -30°C to 30°C, flow	1.4E-05	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	6.E-05	1/°C	ASTM D 696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	260	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	212	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.37	g/cm³	ASTM D 792
Mold Shrinkage, flow, 24 hrs	0.2 - 0.4	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.7 - 0.9	%	ASTM D 955
Density	1.37	g/cm³	ISO 1183
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	1.E+00 - 3.E+00	Ohm-cm	ASTM D 257
Surface Resistivity	2.E+00 - 4.E+00	Ohm	ASTM D 257
Surface Resistivity, ROA	1.E+00 - 3.E+00	Ohm	IEC 60093
Source GMD, last updated:11/25/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Melt Temperature	315 - 320	°C
Front - Zone 3 Temperature	330 - 345	°C
Middle - Zone 2 Temperature	320 - 330	°C
Rear - Zone 1 Temperature	305 - 315	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:11/25/2008

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon OEL13I.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!