S-Plastic Stat-kon OE008 a compound based on PPS-Linear resin containing Carbon Fiber. Added features include: Electically

Product Categories

Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

Shenzhen Samtion Chemical Co., Ltd

Contact Now

S-Plastic Stat-kon OE008 a compound based on PPS-Linear resin containing Carbon Fiber. Added features include: Electically

Name: SPlastic Statkon OE008 a compound based on PPSLinear resin containing Carbon Fiber Added features include Electically
Brand: S-Plastic Stat-kon
Price: 1 USD

China S-Plastic Stat-kon OE008 a compound based on PPS-Linear resin containing Carbon Fiber. Added features include: Electically wholesale

Brand Name : S-Plastic Stat-kon

Model Number : OE008

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon OE008 resin is a compound based on PPS-Linear resin containing Carbon Fiber. Added features include: Electically

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break, 5 mm/min	178	MPa	ISO 527
Tensile Strain, break, 5 mm/min	0.7	%	ISO 527
Tensile Modulus, 1 mm/min	30300	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	253	MPa	ISO 178
Flexural Stress, break, 2 mm/min	251	MPa	ISO 178
Flexural Modulus, 2 mm/min	25300	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	20	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
CTE, 23°C to 60°C, flow	5.E-06	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	3.9E-05	1/°C	ISO 11359-2
PHYSICAL	Value	Unit	Standard
Mold Shrinkage, flow	0.1	%	S-Plastics Method
Density	1.46	g/cm³	ISO 1183
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+01 - 1.E+03	Ohm	ASTM D 257
Source GMD, last updated:11/13/2007

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Melt Temperature	315 - 320	°C
Front - Zone 3 Temperature	330 - 345	°C
Middle - Zone 2 Temperature	320 - 330	°C
Rear - Zone 1 Temperature	305 - 315	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:11/13/2007

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon OE008.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!