S-Plastic Stat-kon KX02764 a compound based on Acetal resin containing Carbon Powder. Added features of this material includ

Product Categories

Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

Shenzhen Samtion Chemical Co., Ltd

Contact Now

S-Plastic Stat-kon KX02764 a compound based on Acetal resin containing Carbon Powder. Added features of this material includ

Name: SPlastic Statkon KX02764 a compound based on Acetal resin containing Carbon Powder Added features of this material includ
Brand: S-Plastic Stat-kon
Price: 1 USD

China S-Plastic Stat-kon KX02764 a compound based on Acetal resin containing Carbon Powder. Added features of this material includ wholesale

Brand Name : S-Plastic Stat-kon

Model Number : KX02764

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon KX02764 resin is a compound based on Acetal resin containing Carbon Powder. Added features of this material include:

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	53	MPa	ASTM D 638
Tensile Stress, break	47	MPa	ASTM D 638
Tensile Strain, yield	3.8	%	ASTM D 638
Tensile Strain, break	10.2	%	ASTM D 638
Tensile Modulus, 50 mm/min	3480	MPa	ASTM D 638
Flexural Stress	100	MPa	ASTM D 790
Flexural Modulus	3010	MPa	ASTM D 790
Tensile Stress, yield	53	MPa	ISO 527
Tensile Stress, break	46	MPa	ISO 527
Tensile Strain, yield	4	%	ISO 527
Tensile Strain, break	18.1	%	ISO 527
Tensile Modulus, 1 mm/min	3460	MPa	ISO 527
Flexural Stress	96	MPa	ISO 178
Flexural Modulus	3010	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	373	J/m	ASTM D 4812
Izod Impact, notched, 23°C	42	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	3	J	ASTM D 3763
Multiaxial Impact	7	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	52	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	4	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	106	°C	ASTM D 648
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	103	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.443	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.18	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	1.5 - 3.5	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1.5 - 3.5	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	1.5 - 3.5	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.5 - 3.5	%	ISO 294
Density	1.43	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.25	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	1.E+02 - 1.E+06	Ohm-cm	ASTM D 257
Surface Resistivity	1.E+02 - 1.E+06	Ohm	ASTM D 257
Source GMD, last updated:10/01/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Melt Temperature	200 - 215	°C
Front - Zone 3 Temperature	210 - 220	°C
Middle - Zone 2 Temperature	195 - 205	°C
Rear - Zone 1 Temperature	175 - 190	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:10/01/2004

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon KX02764.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!