S-Plastic Stat-kon IS000LX is a compound based on Nylon 6/12 containing Stainless Steel Fibers.

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Stat-kon IS000LX is a compound based on Nylon 6/12 containing Stainless Steel Fibers.

Name: SPlastic Statkon IS000LX is a compound based on Nylon 612 containing Stainless Steel Fibers
Brand: S-Plastic Stat-kon
Price: 1 USD

China S-Plastic Stat-kon IS000LX is a compound based on Nylon 6/12 containing Stainless Steel Fibers. wholesale

Brand Name : S-Plastic Stat-kon

Model Number : IS000LX

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon IS000LX resin is a compound based on Nylon 6/12 containing Stainless Steel Fibers.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	67	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	9.3	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	10.2	%	ASTM D 638
Tensile Modulus, 50 mm/min	3040	MPa	ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span	2670	MPa	ASTM D 790
Tensile Stress, break, 5 mm/min	66	MPa	ISO 527
Tensile Strain, break, 5 mm/min	8.5	%	ISO 527
Tensile Modulus, 1 mm/min	3070	MPa	ISO 527
Flexural Stress	82	MPa	ISO 178
Flexural Modulus, 2 mm/min	2430	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	486	J/m	ASTM D 4812
Izod Impact, notched, 23°C	27	J/m	ASTM D 256
Multiaxial Impact	0	J	ISO 6603
Instrumented Impact Total Energy, 23°C	2	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	35	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	3	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	180	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	92	°C	ASTM D 648
CTE, -30°C to 30°C, flow	1.02E-04	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	1.19E-04	1/°C	ASTM D 696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	161	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	72	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.18	-	ASTM D 792
Density	1.18	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.2	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)	1 - 3	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	2 - 4	%	ASTM D 955
Moisture Absorption (23°C / 50% RH)	0.29	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+02 - 1.E+06	Ohm	ASTM D 257
Source GMD, last updated:2010/04/05

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.12 - 0.2	%
Melt Temperature	270 - 275	°C
Front - Zone 3 Temperature	270 - 280	°C
Middle - Zone 2 Temperature	260 - 270	°C
Rear - Zone 1 Temperature	255 - 265	°C
Mold Temperature	65 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:2010/04/05

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon IS000LX.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!