S-Plastic Stat-kon DX05474 a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features

Name: SPlastic Statkon DX05474 a compound based on Polycarbonate resin containing Flame Retardant Carbon Fiber Added features
Brand: S-Plastic Stat-kon
Price: 1 USD

China S-Plastic Stat-kon DX05474 a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features wholesale

Brand Name : S-Plastic Stat-kon

Model Number : DX05474

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon DX05474 resin is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Flame Retardant, Mold Release.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, break	105	MPa	ASTM D 638
Tensile Strain, break	5.9	%	ASTM D 638
Tensile Modulus, 50 mm/min	13780	MPa	ASTM D 638
Flexural Stress	158	MPa	ASTM D 790
Flexural Modulus	7580	MPa	ASTM D 790
Tensile Stress, break	107	MPa	ISO 527
Tensile Strain, break	6.4	%	ISO 527
Tensile Modulus, 1 mm/min	7680	MPa	ISO 527
Flexural Stress	169	MPa	ISO 178
Flexural Modulus	7300	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	373	J/m	ASTM D 4812
Izod Impact, notched, 23°C	53	J/m	ASTM D 256
Izod Impact, unnotched 80104 +23°C	28	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	8	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	295	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	290	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.03E-04	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	4.14E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	1.03E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	4.1E-05	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	150	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	146	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.29	g/cm³	ASTM D 792
Mold Shrinkage, flow, 24 hrs	0.3 - 0.5	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.4 - 0.6	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.36	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.51	%	ISO 294
Density	1.29	g/cm³	ISO 1183
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+03 - 1.E+07	Ohm	ASTM D 257
Source GMD, last updated:09/24/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/24/2008

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon DX05474.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!