S-Plastic Stat-kon DX98477 a compound based on Polycarbonate containing proprietary fillers. Characteristics of this grade a

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Stat-kon DX98477 a compound based on Polycarbonate containing proprietary fillers. Characteristics of this grade a

Name: SPlastic Statkon DX98477 a compound based on Polycarbonate containing proprietary fillers Characteristics of this grade a
Brand: S-Plastic Stat-kon
Price: 1 USD

China S-Plastic Stat-kon DX98477 a compound based on Polycarbonate containing proprietary fillers. Characteristics of this grade a wholesale

Brand Name : S-Plastic Stat-kon

Model Number : DX98477

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon DX98477 resin is a compound based on Polycarbonate containing proprietary fillers. Characteristics of this grade are Statically

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	59	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	49	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	4.8	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	21.2	%	ASTM D 638
Tensile Modulus, 50 mm/min	2790	MPa	ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span	2890	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	58	MPa	ISO 527
Tensile Stress, break, 5 mm/min	46	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	4.7	%	ISO 527
Tensile Strain, break, 5 mm/min	21.4	%	ISO 527
Tensile Modulus, 1 mm/min	2700	MPa	ISO 527
Flexural Stress	89	MPa	ISO 178
Flexural Modulus, 2 mm/min	2720	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	2330	J/m	ASTM D 4812
Izod Impact, notched, 23°C	87	J/m	ASTM D 256
Multiaxial Impact	34	J	ISO 6603
Instrumented Impact Total Energy, 23°C	45	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	234	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	10	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	142	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	133	°C	ASTM D 648
CTE, -30°C to 30°C, flow	6.7E-05	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	6.6E-05	1/°C	ASTM D 696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	142	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	132	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.25	-	ASTM D 792
Density	1.25	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.16	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)	0.8 - 1	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	0.8 - 1	%	ASTM D 955
Moisture Absorption (23°C / 50% RH)	0.24	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	2.E+00 - 6.E+00	Ohm	ASTM D 257
Source GMD, last updated:2010/07/19

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:2010/07/19

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon DX98477.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!