S-Plastic Stat-kon DE002P is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this materia

Product Categories

Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

Shenzhen Samtion Chemical Co., Ltd

Contact Now

S-Plastic Stat-kon DE002P is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this materia

Name: SPlastic Statkon DE002P is a compound based on Polycarbonate resin containing Carbon Fiber Added features of this materia
Brand: S-Plastic Stat-kon
Price: 1 USD

China S-Plastic Stat-kon DE002P is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this materia wholesale

Brand Name : S-Plastic Stat-kon

Model Number : DE002P

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Compliant, 94V-2 Flame Class Rating (3)(4) : 1.5

Contact Now

S-Plastics Stat-kon DE002P resin is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include:

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	115	MPa	ASTM D 638
Tensile Strain, break	2.4	%	ASTM D 638
Tensile Modulus, 50 mm/min	8680	MPa	ASTM D 638
Flexural Stress	185	MPa	ASTM D 790
Flexural Modulus	7370	MPa	ASTM D 790
Tensile Stress, break	118	MPa	ISO 527
Tensile Strain, break	2.5	%	ISO 527
Tensile Modulus, 1 mm/min	8500	MPa	ISO 527
Flexural Stress	189	MPa	ISO 178
Flexural Modulus	8500	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	491	J/m	ASTM D 4812
Izod Impact, notched, 23°C	64	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	14	J	ASTM D 3763
Multiaxial Impact	4	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	34	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	7	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	143	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	140	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.8E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	3.83E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	1.8E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	3.83E-05	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	143	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	139	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.23	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.12	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.1 - 0.3	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.2 - 0.4	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.06 - 0.32	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.29 - 0.43	%	ISO 294
Density	1.23	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.2	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+02 - 1.E+06	Ohm	ASTM D 257
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant, 94V-2 Flame Class Rating (3)(4)	1.5	mm	UL 94 by GE
Source GMD, last updated:09/30/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/30/2004

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon DE002P.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!