S-Plastic Stat-kon DD000 a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material i

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Stat-kon DD000 a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material i

Name: SPlastic Statkon DD000 a compound based on Polycarbonate resin containing Carbon Powder Added features of this material i
Brand: S-Plastic Stat-kon
Price: 1 USD

China S-Plastic Stat-kon DD000 a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material i wholesale

Brand Name : S-Plastic Stat-kon

Model Number : DD000

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Compliant, 94HB Flame Class Rating (3)(4) : 1.5

Contact Now

S-Plastics Stat-kon DD000 resin is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material
include: Electrically Conductive.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	62	MPa	ASTM D 638
Tensile Stress, break	56	MPa	ASTM D 638
Tensile Strain, yield	4.9	%	ASTM D 638
Tensile Strain, break	9.5	%	ASTM D 638
Tensile Modulus, 50 mm/min	2680	MPa	ASTM D 638
Flexural Stress	102	MPa	ASTM D 790
Flexural Modulus	2890	MPa	ASTM D 790
Tensile Stress, yield	60	MPa	ISO 527
Tensile Stress, break	53	MPa	ISO 527
Tensile Strain, yield	4.4	%	ISO 527
Tensile Strain, break	8.8	%	ISO 527
Tensile Modulus, 1 mm/min	2900	MPa	ISO 527
Flexural Stress	102	MPa	ISO 178
Flexural Modulus	3100	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	1217	J/m	ASTM D 4812
Izod Impact, notched, 23°C	64	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	8	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	98	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	138	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	127	°C	ASTM D 648
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	127	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.24	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.14	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.8	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.8	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.84	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.82	%	ISO 294
Moisture Absorption (23°C / 50% RH)	0.25	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+02 - 1.E+06	Ohm	ASTM D 257
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant, 94HB Flame Class Rating (3)(4)	1.5	mm	UL 94 by GE
Source GMD, last updated:09/30/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/30/2004

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon DD000.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!